Introduction

PTFE - Polytetrafluorethylene can truly be described by that much used word "unique". No other plastics material, indeed no other material of any kind, can match its combination of properties.

Canflon® high performance products are typically composed of woven fibers -like glass coated with PTFE.

Canflon® PTFE coated glass fabrics are available in wide range of grades and qualities; A variety of thickness, substrate, weights and surface textures can be produced, in a diversity of styles.
 
Properties
  • Outstanding heat and cold resistance (from -170ºC to +260ºC)
  • Excellent chemical resistance
  • Non-stick surface, easy to clean
  • High dielectric strength
  • Dimensional stability
  • Resistance to UV, IR and HF
  • Non-toxic
 
Canflon® Data Sheet
STYLE

NOMINAL
THICKNESS

NOMINAL
WEIGHT
gr/m²

PTFE
CONTENT
%

STANDART
WIDTHS
mm

TENSILES
N/5 cm

OTHER
PROPERTIES
Plain Fabrics    
Dielectric Volts
108.08
0.080
155
68
1000-1500
800
2600
208.08
0.075
135
64
1000         
800
-
308.08
0.070
105
53
1000         
800
-
216.13
0.130
270
60
1000         
1200
3000
316.13
0.120
240
54
1000-1500
1200
-
416.13
0.110
220
48
1000-1240
1200
-
116.15
0.150
320
67
1000         
1200
4000
216.15
0.140
296
63
1000         
1200
-
116.15SP
0.140
296
63
1000         
1200
-
828.25
0.250
530
62
1000-1200
2300
4000
728.25
0.240
490
59
1000         
2300
-
628.25
0.220
455
55
1000         
2300
-
828.25 red
0.270
585
66
1500         
2300
food grade
141.36
0.330
620
54
1000-1500
3300
2400
Conductive Fabrics (Antistatic)
108.08AS
0.080
155
68
1000         
800 
-
216.13AS
0.127
255
58
1000         
1200
-
828.25AS
0.250
530
62
2000         
2300
-
728.25AS
0.245
510
60
1500         
2300
-
628.25AS
0.230
480
58
1000         
2300
-
141.36AS
0.350
710
59
1500-2000
2300
-
Porous Fabrics
408.08
0.070
  
75
36
1000         
800
516.13
0.110
133
21
1000         
1200
428.25
0.220
278
51
1000         
2300
Tear Resistant Fabrics
Trap. Tear Strength (N)
116.13TR
0.127
255
59
1000        
1200
45x50
628.25TR
0.230
480
58
1000        
2300
90x95
Open-Mesh PTFE / Glass Fabrics
Mesh Size
9002
0.900
460
31
1800-2050-2500-2750-3200
2500
4x4
304
0.750
530
22
1500-1600                            
2500
1x1
9004
0.800
430
27
2100-2500-3000                   
3000
2x2
9009
1.200
550
31
2500-3350                            
3000
6x6
9012
1.200
580
31
2050-2500-3350                   
3000
4x4
9002AS (antistatic)
0.900
460
31
2500-2750                            
2500
4x4
Open-Mesh PTFE Aramid® - Glass Fabrics
9005
1.200
630
30
2000-3000       
5000
5x4
Open-Mesh PTFE Aramid® Fabrics
9003
0.750
280
27
2200-2600-300
3500
4x4
9007
0.870
407
32
3350                
8000
2x3
Open-Mesh PTFE Aramid® - Glass Fabrics
9008
1.200
680
31
3250               
2500
4x4
PTFE Aramid® Fabrics
04613KS
0.158
220
1250
04612
0.370
530
1000
04614
0.440
680
1600
04614AS
0.440
680
1600
antistatic
04613AS
0.160
230
1250
antistatic
Other Grades
03802
0.800
1100
2000
306
0.865
670
1500-1680
91117
0.365
518
1600
Architectural Grades
Place ask your  specific requirements.
All technical data are based on average values. These values are not intended for use in preparing specifications. Technical information contained herein are based on test results Canada Plastics & Belting believes to be reliable, but they are not to be construed in any manner as warranties expressed.